Description | Conducting Polymer. Greater than 98.5% head-to-tail regiospecific conformation. Forms a shiny red-purple film. |
---|---|
Molecular Weight | average Mw ~60,000 |
Solubility | chloroform: soluble |
Appearance | Solid |
Application | Rechargeable battery electrodes, electrochromic devices, chemical and optical sensors, light-emitting diodes, microelectrical amplifiers, field-effect transistors and non-linear optical materials. Conducting polymer. Rechargeable battery electrodes, electrochromic devices, chemical and optical sensors, light-emitting diodes, microelectrical amplifiers, field-effect transistors and non-linear optical materials. |
Storage | room temp |
Assay | 99.995% trace metals basis |
Fluorescence | λex 416 nm; λem 545 nm in chloroform |
Form | solid,ITO/PEDOT:PSS/P3DDT/PC61BM (1:3)/LiF/Al[8]• Short-circuit current density (Jsc): 2.9 mA/cm2 • Open-circuit voltage (Voc): 0.6 V• Fill Factor (FF): 0.38• Power Conversion Efficiency (PCE): 0.65 % |
Grade | electronic grade |
MDL Number | MFCD00677714 |
OPV Device Performance | ITO/PEDOT:PSS/P3DDT/PC61BM (1:3)/LiF/Al • Short-circuit current density (Jsc): 2.9 mA/cm2 • Open-circuit voltage (Voc): 0.6 V • Fill Factor (FF): 0.38 • Power Conversion Efficiency (PCE): 0.65 % |
Orbital Energy | HOMO -5.29 eV |
Packaging | 250 mg in glass insert |
Quality Level | 100 |
Semiconductor Properties | P-type (mobility=1E-4-1E-1 cm2/V·s) |
Transition Temperature | Tm (DSC) 165.6 °C (peak) |